ANSI B16.9 ASTM A403 WP310S 90Deg LR Elbow DN50 Sch40S
Short Description
Model No.: WP310S-90Deg-LR-Elbow-DN50-Sch40S
China Elbow Manufacturer www.metallicsteel.com offers ANSI B16.9 ASTM A403 WP310S 90Deg LR Elbow, DN50, Sch40S.
Key Specifications / Features
Type: 90Deg LR Elbow
Material: 310S
Degree: 90 Degree
Size: 2 inch (DN50)
Standard: ANSI B16.9, THK: Sch40S
Ends: BW
Chemical composition % of grade 310 and 310S stainless steel
Chemical Composition
310
310S
Carbon
0.25 max
0.08 max
Manganese
2.00 max
2.00 max
Silicon
1.50 max
1.50 max
Phosphorus
0.045 max
0.045 max
Sulphur
0.030 max
0.030 max
Chromium
24.00 – 26.00
24.00 – 26.00
Nickel
19.00 – 22.00
19.00 – 22.00
Chemical composition % of grade 310 and 310S stainless steel
|
Chemical Composition |
310 |
310S |
|
Carbon |
0.25 max |
0.08 max |
|
Manganese |
2.00 max |
2.00 max |
|
Silicon |
1.50 max |
1.50 max |
|
Phosphorus |
0.045 max |
0.045 max |
|
Sulphur |
0.030 max |
0.030 max |
|
Chromium |
24.00 – 26.00 |
24.00 – 26.00 |
|
Nickel |
19.00 – 22.00 |
19.00 – 22.00 |
Mechanical properties of of grade 310/310S stainless steel
Mechanical Properties
310/ 310S
Grade 0.2 % Proof Stress MPa (min)
205
Tensile Strength MPa (min)
520
Elongation % (min)
40
Hardness (HV) (max)
225
Mechanical properties of of grade 310/310S stainless steel
|
Mechanical Properties |
310/ 310S |
|
Grade 0.2 % Proof Stress MPa (min) |
205 |
|
Tensile Strength MPa (min) |
520 |
|
Elongation % (min) |
40 |
|
Hardness (HV) (max) |
225 |
Physical properties of grade 310/310S stainless steel
Properties
at
Value
Unit
Density
8,000
Kg/m3
Electrical Conductivity
25°C
1.25
%IACS
Electrical Resistivity
25°C
0.78
Micro ohm.m
Modulus of Elasticity
20°C
200
GPa
Shear Modulus
20°C
77
GPa
Poisson’s Ratio
20°C
0.30
Melting Rnage
1400-1450
°C
Specific Heat
500
J/kg.°C
Relative Magnetic Permeability
1.02
Thermal Conductivity
100°C
14.2
W/m.°C
Coefficient of Expansion
0-100°C
15.9
/°C
0-315°C
16.2
/°C
0-540°C
17.0
/°C
Physical properties of grade 310/310S stainless steel
|
Properties |
at |
Value |
Unit |
|
Density |
|
8,000 |
Kg/m3 |
|
Electrical Conductivity |
25°C |
1.25 |
%IACS |
|
Electrical Resistivity |
25°C |
0.78 |
Micro ohm.m |
|
Modulus of Elasticity |
20°C |
200 |
GPa |
|
Shear Modulus |
20°C |
77 |
GPa |
|
Poisson’s Ratio |
20°C |
0.30 |
|
|
Melting Rnage |
|
1400-1450 |
°C |
|
Specific Heat |
|
500 |
J/kg.°C |
|
Relative Magnetic Permeability |
|
1.02 |
|
|
Thermal Conductivity |
100°C |
14.2 |
W/m.°C |
|
Coefficient of Expansion |
0-100°C |
15.9 |
/°C |
|
|
0-315°C |
16.2 |
/°C |
|
|
0-540°C |
17.0 |
/°C |