ANSI B16.9 ASTM A403 WP304 ECC RED 6 Inch – 4 Inch SCH10S
Short Description
Model No.: WP304-ECC-RED-6-Inch-4-Inch-SCH10S
China ECC RED Manufacturer www.metallicsteel.com offers ANSI B16.9 ASTM A403 WP304 ECC RED, 6 Inch – 4 Inch, SCH10S.
Key Specifications / Features
Type: ECC RED
Schedule: SCH10S
Material: 304
Ends: BW
Standard: ANSI B16.9
Size: 6 Inch – 4 Inch
Composition ranges for 304 grade stainless steel
Grade
C
Mn
Si
P
S
Cr
Mo
Ni
N
304
min.
max.
–
0.08
–
2.0
–
0.75
–
0.045
–
0.030
18.0
20.0
–
8.0
10.5
–
0.10
304L
min.
max.
–
0.030
–
2.0
–
0.75
–
0.045
–
0.030
18.0
20.0
–
8.0
12.0
–
0.10
304H
min.
max.
0.04
0.10
–
2.0
–
0.75
-0.045
–
0.030
18.0
20.0
–
8.0
10.5
–
Mechanical properties of 304 grade stainless steel
Grade
Tensile Strength (MPa) min
Yield Strength 0.2% Proof (MPa) min
Elongation (% in 50mm) min
Hardness
Rockwell B (HR B) max
Brinell (HB) max
304
515
205
40
92
201
304L
485
170
40
92
201
304H
515
205
40
92
201
304H also has a requirement for a grain size of ASTM No 7 or coarser.
Physical properties of 304 grade stainless steel in the annealed condition
Grade
Density (kg/m3)
Elastic Modulus (GPa)
Mean Coefficient of Thermal Expansion (μm/m/°C)
Thermal Conductivity (W/m.K)
Specific Heat 0-100°C (J/kg.K)
Electrical Resistivity (nΩ.m)
0-100°C
0-315°C
0-538°C
at 100°C
at 500°C
304/L/H
8000
193
17.2
17.8
18.4
16.2
21.5
500
720
Grade specifications for 304 grade stainless steel
Grade
UNS No
Old British
Euronorm
Swedish SS
Japanese JIS
BS
En
No
Name
304
S30400
304S31
58E
1.4301
X5CrNi18-10
2332
SUS 304
304L
S30403
304S11
–
1.4306
X2CrNi19-11
2352
SUS 304L
304H
S30409
304S51
–
1.4948
X6CrNi18-11
–
–
These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.
Composition ranges for 304 grade stainless steel
Grade
C
Mn
Si
P
S
Cr
Mo
Ni
N
304
min.
max.
–
0.08
–
2.0
–
0.75
–
0.045
–
0.030
18.0
20.0
–
8.0
10.5
–
0.10
304L
min.
max.
–
0.030
–
2.0
–
0.75
–
0.045
–
0.030
18.0
20.0
–
8.0
12.0
–
0.10
304H
min.
max.
0.04
0.10
–
2.0
–
0.75
-0.045
–
0.030
18.0
20.0
–
8.0
10.5
–
Composition ranges for 304 grade stainless steel
|
Grade |
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
N |
|
|
304 |
min. max. |
– 0.08 |
– 2.0 |
– 0.75 |
– 0.045 |
– 0.030 |
18.0 20.0 |
– |
8.0 10.5 |
– 0.10 |
|
304L |
min. max. |
– 0.030 |
– 2.0 |
– 0.75 |
– 0.045 |
– 0.030 |
18.0 20.0 |
– |
8.0 12.0 |
– 0.10 |
|
304H |
min. max. |
0.04 0.10 |
– 2.0 |
– 0.75 |
-0.045 |
– 0.030 |
18.0 20.0 |
– |
8.0 10.5 |
– |
Mechanical properties of 304 grade stainless steel
Grade
Tensile Strength (MPa) min
Yield Strength 0.2% Proof (MPa) min
Elongation (% in 50mm) min
Hardness
Rockwell B (HR B) max
Brinell (HB) max
304
515
205
40
92
201
304L
485
170
40
92
201
304H
515
205
40
92
201
304H also has a requirement for a grain size of ASTM No 7 or coarser.
|
Grade |
Tensile Strength (MPa) min |
Yield Strength 0.2% Proof (MPa) min |
Elongation (% in 50mm) min |
Hardness |
|
|
Rockwell B (HR B) max |
Brinell (HB) max |
||||
|
304 |
515 |
205 |
40 |
92 |
201 |
|
304L |
485 |
170 |
40 |
92 |
201 |
|
304H |
515 |
205 |
40 |
92 |
201 |
|
304H also has a requirement for a grain size of ASTM No 7 or coarser. |
|||||
Physical properties of 304 grade stainless steel in the annealed condition
Grade
Density (kg/m3)
Elastic Modulus (GPa)
Mean Coefficient of Thermal Expansion (μm/m/°C)
Thermal Conductivity (W/m.K)
Specific Heat 0-100°C (J/kg.K)
Electrical Resistivity (nΩ.m)
0-100°C
0-315°C
0-538°C
at 100°C
at 500°C
304/L/H
8000
193
17.2
17.8
18.4
16.2
21.5
500
720
|
Grade |
Density (kg/m3) |
Elastic Modulus (GPa) |
Mean Coefficient of Thermal Expansion (μm/m/°C) |
Thermal Conductivity (W/m.K) |
Specific Heat 0-100°C (J/kg.K) |
Electrical Resistivity (nΩ.m) |
|||
|
0-100°C |
0-315°C |
0-538°C |
at 100°C |
at 500°C |
|||||
|
304/L/H |
8000 |
193 |
17.2 |
17.8 |
18.4 |
16.2 |
21.5 |
500 |
720 |
Grade specifications for 304 grade stainless steel
Grade
UNS No
Old British
Euronorm
Swedish SS
Japanese JIS
BS
En
No
Name
304
S30400
304S31
58E
1.4301
X5CrNi18-10
2332
SUS 304
304L
S30403
304S11
–
1.4306
X2CrNi19-11
2352
SUS 304L
304H
S30409
304S51
–
1.4948
X6CrNi18-11
–
–
These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.
|
Grade |
UNS No |
Old British |
Euronorm |
Swedish SS |
Japanese JIS |
||
|
BS |
En |
No |
Name |
||||
|
304 |
S30400 |
304S31 |
58E |
1.4301 |
X5CrNi18-10 |
2332 |
SUS 304 |
|
304L |
S30403 |
304S11 |
– |
1.4306 |
X2CrNi19-11 |
2352 |
SUS 304L |
|
304H |
S30409 |
304S51 |
– |
1.4948 |
X6CrNi18-11 |
– |
– |
|
These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted. |
|||||||